| BN-2 | BN-4 | BN-6 | BN-8 | BN-8A | BN-9 | BN-9H | BN-10 | BN-11 | BN-12D | BN-12L | |
Potongan residu Br | Mt GS | 300-400 3.0-4.0 | 460-520 4.6-5.2 | 550-650 5.5-6.5 | 620-670 6.2-6.7 | 620-680 6.2-6.8 | 650-700 6.5-7.0 | 650-700 6.5-7.0 | 670-720 6.7-7.2 | 680-740 6.8-7.4 | 720-770 7.2-7.7 | 730-770 7.3-7.7 |
Kesukaan Hcb | KA/m. KONe | 160-240 2.0-3.0 | 224-288 2.8-3.6 | 320-376 4.0-4.7 | 400-456 5.0-5.7 | 400-480 5.0-6.0 | 416-456 5.2-5.7 | 432-488 5.4-6.1 | 424-480 5.3-6.0 | 400-480 5.0-6.0 | 440-520 5.5-6.5 | 368-432 4.6-5.4 |
Kesukaan intrinsik Hcj | KA/m. KONe | 440-600 5.5-7.5 | 504-680 6.3-8.5 | 600-720 7.5-9.0 | 640-800 8.0-10.0 | 1040-1280 13.0-16.0 | 680-800 8.5-10.0 | 920-1040 11.5-13.0 | 640-800 8.0-10.0 | 640-800 8.0-10.0 | 720-880 9.0-11.0 | 520-640 6.5-8.0 |
Maks. Produk Energi (BH)maks | KJ/m3 GOCR | 19-26 2.4-3.3 | 30-35 3.8-4.4 | 44-52 5.5-6.5 | 64-76 8.0-9.5 | 65-73 8.2-9.2 | 68-76 8.5-9.5 | 71-80 8.9-10.0 | 76-84 9.5-10.5 | 80-88 10.0-11.0 | 88-96 11.0-12.0 | 80-88 10.0-11.0 |
Kerapatan ρ | g/cm3 | 5.6-6.0 | 5.6-6.0 | 5.6-6.0 | 5.8-6.2 | 5.8-6.1 | 5.8-6.2 | 5.8-6.1 | 5.8-6.2 | 6.0-6.2 | 6.1-6.3 | 6.0-6.3 |
Daya meoil μr | %/CELCIUS | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 |
Mereka. Efisiensi: Br | -0,11 | -0,11 | -0,11 | -0,11 | -0,10 | -0,11 | -0,10 | -0,10 | -0,10 | -0,10 | -0,13 | |
Curie Tem. TC | 300 | 300 | 300 | 300 | 350 | 300 | 350 | 350 | 350 | 350 | 320 | |
Maks. Mengoperasikan em. TW |
| 160 | 160 | 160 | 160 | 180 | 160 | 180 | 160 | 160 | 160 | 120 |
| BZ-3 | BZ-4 | BZ-5 | BZ-6 | BZ-7 | BZ-5SR(PPS) | BZ-6SR(PPS) | |
Potongan residu Br | Mt GS | 350-450 3.5-4.5 | 400-500 4.0-5.0 | 450-550 4.5-5.5 | 500-600 5.0-6.0 | 550-650 5.5-6.5 | 450-550 4.5-5.5 | 500-600 5.0-6.0 |
Kesukaan Hcb | KA/m. KONe | 200-280 2.5-3.5 | 240-320 3.0-4.0 | 304-360 3.8-4.5 | 328-384 4.1-4.8 | 344-400 4.3-5.0 | 320-400 4.0-5.0 | 320-400 4.0-5.0 |
Kesukaan intrinsik Hcj | KA/m. KONe | 400-640 5.0-8.0 | 560-720 7.0-9.0 | 640-800 8.0-10.0 | 640-800 8.0-10.0 | 640-800 8.0-10.0 | 880-1120 11.0-14.0 | 880-1120 11.0-14.0 |
Maks. Produk Energi (BH)maks | KJ/m3 GOCR | 20-28 2.5-3.5 | 28-36 3.5-4.5 | 36-44 4.5-5.5 | 44-52 5.5-6.5 | 52-60 6.5-7.5 | 36-44 4.5-5.5 | 44-52 5.5-6.5 |
Kerapatan ρ | g/cm3 | 4.5-5.0 | 4.5-5.0 | 4.5-5.1 | 4.7-5.2 | 4.7-5.3 | 4.8-5.3 | 4.9-5.4 |
Daya meoil μr | %/CELCIUS | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 |
Mereka. Efisiensi: Br | -0,11 | -0,11 | -0,11 | -0,11 | -0,10 | -0,11 | -0,10 | |
Maks. Mengoperasikan em. TW |
| 120 | 120 | 120 | 120 | 120 | 180 | 180 |
Nama teknologi | Pengenalan | Lingkup yang berlaku | Fitur |
Lapisan Electropetik | Teknik yang paling umum digunakan di industri. | Penerapan di sebagian besar magnet kompresi. |
|
Lapisan semprotan | Semprot Cat anti-korosi epoksi ke permukaan magnet kompresi. | Terapkan ke bagian kerja berukuran kecil, terutama untuk magnet kompresi busur. |
|
Kegiatan ini juga dapat digunakan sebagai oli rendam anti karat | Lapisan anti karat dapat sangat meningkatkan kemampuan anti karat pada magnet kompresi. | Terutama cocok untuk magnet kompresi berdiameter dalam. |
|
Filtrasi | Menyusup ke dalam kekosongan magnet kompresi oleh tekanan negatif. | Terapkan ke lingkungan ekstrem, seperti oli atau pelarut. |
|